Quantity(Piece/Pieces) | 1 ~ 1000 | >1000 |
Est. Time(days) | 7 | To be negotiated |
If you finish the payment today, your order will ship out within the delivery date.
Glass Fiber P-Glass 3D Printer Filament 1.75mm High Transparency light PC & PETG Composite better than ABS PLA 1kg best sellers
1. Basic introduction to P-glass: The composite polymer material of PC and PETG imitates glass material; it has high transparency, good rigidity, toughness and strength; its transmittance is more than 92%, haze is 0.2%, and its optical performance is better than that of glass. . 2. P-glass parameters: Color: transparent Wire diameter: 1.75mm/3mm Net weight: 1kg, gross weight: 1.4kg Printing temperature: 200-220 ° C Hot bed temperature: 60-100c Printing thickness: 0.3mm/0.5mm thick shell, strong and rigid 3. P-glass printing test experience: (1) Temperature test: wire comparison from 170 ° C, 180 ° C, 190 ° C, 200 ° C, 210 ° C It is impossible to melt and extrude if the wire does not come out below 170 ° C; 170 / 180 / 190C extrusion is white (may be incomplete melting), and the transparency is not enough. Some of them are similar to the type of PLA transparent material extrusion, and the surface is Matt, without luster; At 200 ° C / 210 ° C, the wire is transparent, glossy and bright, and the transparency is similar to that of P-glass; Therefore, the printing range of 200-220c is recommended from the temperature test; (2) Printing difficulty: P-glass printing difficulty coefficient is higher than PLA, but it is still easy to print. The material itself has better rigidity, firmness and toughness than PLA. It can print thin shell objects, or single-layer appearance. Thin wall less than 1mm can also be printed. Test printing The wall thickness of the vase is less than 0.5mm, so it is hard and rigid to print. If it is printed with PLA, it may be easy to crack, and P-glass is very strong. However, when printing with P-glass, pay attention to the first few layers of the bottom contacting the platform. When the printer is leveling, the distance between the nozzle and the platform shall be well controlled, The distance is too large, P-glass is easy to be extruded, cooled, curled on the platform, curled on the nozzle with high temperature, and dragged away, resulting in unsuccessful printing of the previous layers; If the distance is too close to the platform when the nozzle is leveled, the front layers will lead to poor silk discharge or few silk discharge when printing, the front layers will not be very flat when printing, the poor silk discharge will lead to more burrs at the bottom, the nozzle will absorb burrs when moving, and the longer printing time will accumulate more and more burrs on the nozzle wall, so it is necessary to peel off the material balls on the nozzle wall in time To avoid affecting the printing effect; So it is the key to grasp the front layers of printing. Once the bottom layers are printed, it is similar to PLA to continue to print on the top layer; (3) It is recommended to print objects with simple structure such as thin shell, water cup, lampshade, etc. and objects with regular direction in each layer. It is not recommended to print objects with complex structure such as: objects with many empty walks and nodes in each layer; the thicker the printing is, the less transparent the P-glass is, the thinner the single layer of objects can be printed, and it is very solid;
Glass Fiber P-Glass 3D Printer Filament 1.75mm High Transparency light PC & PETG Composite better than ABS PLA 1kg best sellers